The structure of cortical bone as revealed by the application of methods for the calcified matrix study.

Calcination and decalcification are basic procedures useful to a morphological approach of a biological, composite material like cortical bone. The study was carried out on a whole human femur conserved in liquid (from an educational collection). Cortical fracturing and SEM observation of vascular canals surface collagen texture was used to study bone deproteination at scalar temperatures (400-1,200°C) and acid bone decalcification at crescent time intervals. Heating burned and vaporized the organic matrix with shrinkage of the bone specimens as documented by the weight loss and transverse surface morphometry. SEM showed a pattern of aligned spherulites at 400°C which maintained the collagen fibrils layout (like a mineral cast), followed by a spherulites fusion progression with the temperature increments. At 1200°C a crystalline-like structure of tightly-packed trapezohendron units. XRD analysis supported the SEM morphology displaying the complete Debey rings of hydroxyapatite and spotted Debey rings of withlockite. Surface Ca and P elution was documented after 12 hr of exposition to the acid solution by dissolution of spherulites and the whole canal surface decalcified in depth after 15 days by SEM-EDAX analysis. The periodic pattern of collagen fibrils was still evident up to 15 days of decalcification together with fine granular deposits of a not-collagenic proteic material, while after 30 days no period was observed in the decalcified fibrils. Collagen mineral cast at 400°C calcination. Complete crystalline transformation at 1200°C. Up to 15 days of decalcification fibrils period maintained.

Thanatophoric dysplasia. Correlation among bone X-ray morphometry, histopathology, and gene analysis.

OBJECTIVE: Documentation through X-ray morphometry and histology of the steady phenotype expressed by FGFR3 gene mutation and interpolation of mechanical factors on spine and long bones dysmorphism. MATERIALS AND METHODS: Long bones and spine of eight thanatophoric dysplasia and three age-matched controls without skeletal dysplasia were studied after pregnancy termination between the 18th and the 22nd week with X-ray morphometry, histology, and molecular analysis. Statistical analysis with comparison between TD cases and controls and intraobserver/interobserver variation were applied to X-ray morphometric data. RESULTS: Generalized shortening of long bones was observed in TD. A variable distribution of axial deformities was correlated with chondrocyte proliferation inhibition, defective seriate cell columns organization, and final formation of the primary metaphyseal trabeculae. The periosteal longitudinal growth was not equally inhibited, so that decoupling with the cartilage growth pattern produced the typical lateral spurs around the metaphyseal growth plates. In spine, platyspondyly was due to a reduced height of the vertebral body anterior ossification center, while its enlargement in the transversal plane was not restricted. The peculiar radiographic and histopathological features of TD bones support the hypothesis of interpolation of mechanical factors with FGFR3 gene mutations. CONCLUSIONS: The correlated observations of X-ray morphometry, histopathology, and gene analysis prompted the following diagnostic workup for TD: (1) prenatal sonography suspicion of skeletal dysplasia; (2) post-mortem X-ray morphometry for provisional diagnosis; (3) confirmation by genetic tests (hot-spot exons 7, 10, 15, and 19 analysis with 80-90% sensibility); (4) in negative cases if histopathology confirms TD diagnosis, research of rare mutations through sequential analysis of FGFR3 gene.